Home / Understanding Welding Slag in Flux-Cored Processes

Understanding Welding Slag in Flux-Cored Processes

Slag is more than a bothersome byproduct. It plays an important role in ensuring good weld quality, and the various slag systems also impact a wire’s welding characteristics.

Posted: December 31, 2020

Some filler metals are formulated with self-peeling slag that releases from the weld on its own.
Slag protects the weld from oxidation and contamination from the atmosphere, and helps keep the molten weld pool in the joint as it cools, which is especially important for out-of-position welding.

WELDING TIPS COLUMN

BY MATT UNDERWOOD

Welders may know slag as a bothersome byproduct of gas- and self-shielded flux-cored processes because it frequently requires chipping or grinding to remove it after welding or between passes. But slag is much more than that. It plays an important role in ensuring good weld quality, and the various slag systems also impact a wire’s welding characteristics.

So, what exactly is slag and what does it do?

Slag by Definition, Purpose and Chemistry

The American Welding Society (AWS) defines slag as “a nonmetallic byproduct of the mutual dissolution of flux with nonmetallic impurities in welding and brazing processes.” In short, it’s the hardened layer left on the top of the weld made during flux-cored welding (FCAW). It’s also present in shielded metal arc welding (SMAW), submerged arc welding (SAW), and other welding and brazing processes. It can have a slightly different makeup depending on process or product.

Removing slag is a mechanical process completed with chipping hammers, wire brushes or wheels, or needle scaler. Some filler metals, however, are formulated with self-peeling slag that releases from the weld on its own.

Slag’s purpose is two-fold. It protects the weld from oxidation and contamination from the atmosphere. It also helps keep the molten weld pool in the joint as it cools, which is especially important for out-of-position welding.

Slag forms when the heat from the arc breaks down the filler metal and the base material to form a molten weld pool. Through thermodynamic processes, elements that aren’t included in the formation of the weld pool are essentially pushed out and forced to the surface. There, the elements solidify into slag that includes nonmetallic elements, such as oxides of aluminum, silicon and calcium oxides; and that may also pull nitrogen, hydrogen and some carbon out with it.

The flux inside of both gas- and self-shielded flux-cored wire impacts the way slag behaves. For example, wires with higher levels of titanium dioxide (TiO2) have faster freezing slag, which makes the wire better for welding out of position. However, too much titanium can make the slag sticky. Wires with higher levels of silica tend to generate slag that’s more difficult to remove, while those with higher levels of lime have slag that’s easier to remove.

Slag Systems and Their Characteristics

Flux-cored wires are available with rutile (acidic) or basic slag systems, each of which impact weldability, including arc performance. Each system has advantages and limitations.

Rutile slag systems are composed mostly of titanium dioxide from the mineral rutile along with other minerals such as silica, alumina or zircon. Wires with a rutile slag system have good weldability with low spatter and a soft arc. They’re considered to have excellent welder appeal because they’re easier to use than flux-cored wires with a basic slag system, particularly out of position.

However, wires with a rutile slag system don’t possess the mechanical properties to achieve low temperature toughness compared to their basic counterparts. Wires with a basic slag system are composed of minerals of alkali elements, such as fluorspar, limestone, magnesite or dolomite. Basic slag systems are highly effective at lowering weld metal oxygen, providing superior weld metal toughness but low freezing temperature slags.

Some of the most common flux-cored wires with rutile slag systems include those classified under AWS A5.20: Specification for Carbon Steel Electrodes for Flux-Cored Arc Welding and feature the designators of T-1, T-9 and T-12.

T-1 wires provide good wetting action and are generally reserved for less critical applications because they don’t offer the best toughness.

T-9 wires meet the same chemistry requirements as T-1 wires, along with additional requirement of 20 ft.-lb. at -20 degrees F for Charpy V-Notch testing.

T-12 wires are very similar to T-1 and T-9 wires, but have been modified to provide similar or better impact properties than the T-9. They also have lower manganese content, which enables them to meet the requirements of ASME Section IX for boiler and pressure vessel welding. They tend to require the base material to be relatively clean to achieve X-ray quality.

Basic slag systems are made up primarily of limestone, particularly calcium carbonate (CaCO3), which helps provide good impact properties at low temperatures. This slag system also produces a low-hydrogen weld deposit to resist hot and cold cracking. Many T-5 wires are limited to flat and horizontal welding positions. Overall, they’re more prone to generating spatter and are considered less welder-friendly than flux-cored wires with a rutile slag system.

Preventing Welding Slag Inclusions

Welding slag inclusions can affect the quality of welds produced with flux-cored processes and occur when the slag becomes trapped in the weld when it solidifies. Several best practices and techniques minimize this risk.

First, always fully remove the slag during multipass welds to prevent it from being trapped inside the weld during subsequent passes.

During flat and horizontal welding, use a drag technique with a gun angle of zero (straight up and down) to 10 degrees. The technique for vertical up may vary according the gas- or self-shielded flux-cored wire being used. A drag technique still works well for vertical-up welding if the wire produces a heavy slag. For T-1 wires in a vertical weld, a zero-degree travel angle usually produces quality bead shapes.

For other wires, such as T-5 wires, a zero-degree travel angle to a slight push (around 5 degrees) works because it puts more heat into the base material, allowing the slag to come to the surface of the weld pool.

Using the right welding parameters and travel speeds are also key to reducing the risk of slag inclusions. Too-fast travel speeds or too-high current (which directly effects wire feed speed) can lead to a convex bead profile with dips at the toes of the weld where slag can be locked in place. Too-low current can cause the same problem.

Too-high voltage tends to make the weld bean more concave, which can sometimes lock slag into the weld as well.

Following Best Practices

As with any welding process, selecting the right flux-cored wire for the application and using it according to the filler metal manufacturer’s recommendation is key to good performance. Knowing the slag type associated with each wire is also important to understanding the wire’s weldability and the amount of post-weld and interpass cleanup that will be required. Always follow cleaning best practices to avoid inclusions that could lead to downtime and costly rework.

Subscribe to learn the latest in manufacturing.

Calendar & Events
Southeast Design – 2-Part Show
September 11 - 12, 2013
Greenville, SC
Mid-Atlantic Design – 2-Part Show
September 25 - 26, 2013
Phoenixville, PA
CMTS of Canada
September 30 - October 3, 2013
Mississauga, Canada
Wisconsin Manufacturing and Technology Show
October 8 - 10, 2013
Wisconsin State Fair Park Exposition Center Halls B&C
DISCOVER 2013
October 8 - 16, 2013
Florence, KY
WESTEC 2013
October 15 - 17, 2013
Los Angeles, CA
SOUTH-TEC
October 29 - 31, 2013
Greenville, SC
New England Design-2-Part Show
October 30 - 31, 2013
Marlborough, MA
DMG / Mori Seiki Manufacturing Days
November 12 - 15, 2013
Mori Seiki Manufacturing – Davis, CA
FABTECH
November 18 - 21, 2013
McCormick Place – Chicago, IL
Midwest Design-2-Part Show
November 20 - 21, 2013
Northern Kentucky Convention Center – Covington, KY
PCD Tool Manufacturing
November 20, 2013
United Grinding North America – Fredricksburg, VA